Light emitting diode having a transparent substrate

ABSTRACT

A light emitting diode having a transparent substrate and a method for manufacturing the same. The light emitting diode is formed by creating two semiconductor multilayers and bonding them. The first semiconductor multilayer is formed on a non-transparent substrate. The second semiconductor multilayer is created by forming an amorphous interface layer on a transparent substrate. The two semiconductor multilayers are bonded and the non-transparent substrate is removed, leaving a semiconductor multilayer with a transparent substrate.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of U.S. Ser. No. 11/724,310, which is a reissue application of U.S. Pat. No. 6,867,426, which claimed foreign priority to TAIWAN 90115871 filed on Jun. 27, 2001.

BACKGROUND OF INVENTION

1. Field of the Invention

The present invention relates to a light emitting diode, more specifically to a light emitting diode having a transparent substrate, and a method for manufacturing the same.

2. Description of the Related Art

Light emitting diodes (LEDs) are employed in a wide variety of applications including optical display devices, traffic lights, data storage equipment, communication devices, illumination apparatuses, and medical treatment equipment. Some of the main goals of engineers who design LEDs are to increase the brightness of the light emitted from LEDs and to reduce the cost of manufacturing LEDs.

U.S. Pat. No. 5,783,477 discloses a method of bonding two compound semiconductor surfaces to produce an ohmic contact interface. The method of manufacturing a prior art LED is to create an ohmic contact interface by aligning the crystallographic orientation and rotational alignment of two semiconductor surfaces and applying uniaxial pressure to the semiconductor wafers at a temperature of 1000□. In actual procedure, however, it is difficult and expensive to align the crystallographic orientation and rotational alignment of the two semiconductor surfaces.

SUMMARY OF INVENTION

It is an objective of the claimed invention to provide a light emitting diode (LED) having a transparent substrate and the method for manufacturing the same. The method involves wafer bonding a transparent substrate with a compound semiconductor multilayer. The compound semiconductor multilayer comprising the LED is grown on a non-transparent substrate. The transparent substrate and the compound semiconductor multilayer are bonded using an amorphous interface layer. After the bonding, the non-transparent substrate is removed, leaving an LED with a transparent substrate. The method according to the claimed invention will simplify the procedure of manufacturing LEDs, thereby reducing costs. The method also solves the problem of aligning the crystallographic orientation and rotational alignment of the two semiconductor surfaces and creates a light emitting diode with an increased luminance.

In the claimed invention, a light emitting diode comprises a sapphire transparent substrate. Formed above the substrate is an indium tin oxide (ITO), a top surface of which comprises a first surface region and a second surface region. On the first surface region, the layers of the semiconductor multilayer stacked from bottom to top are: A p⁺-type contact layer of GaAs, a p-type cladding layer of AlGaInP, a multiple quantum well (MQW) light-emitting layer, an n-type cladding layer of AlGaInP, an n-type stop layer of AlGaAs, and an ITO transparent conductive layer. A first electrode is located on the ITO transparent conductive layer, and a second electrode is located on the second surface region.

The claimed invention also details a method for manufacturing the light emitting diode. The first step is to form a first multilayer on an n-type GaAs semiconductor substrate. An n-type stop layer of AlGaAs is formed on the semiconductor substrate. An n-type cladding layer of AlGaInP is formed on the n-type stop layer. An MQW light-emitting layer of AlGaInP is formed on the n-type cladding layer. A p-type cladding layer of AlGaInP is formed on the MQW light-emitting layer. A p⁺-type contact layer of GaAs is formed on the p-type cladding layer. A second multilayer is formed on a sapphire substrate. An amorphous interface layer of ITO IS formed on the sapphire substrate. A third multilayer is produced by placing the first multilayer on the second multilayer and bonding the first multilayer to the second multilayer by elevating temperature. Next, the n-type GaAs semiconductor substrate of the newly created third multilayer is removed, and an ITO transparent conductive layer is formed on the stop layer to produce a fourth multilayer. Next, an exposed interface region is formed by etching away a portion of the fourth multilayer from the ITO transparent conductive layer to the ITO amorphous interface layer. Finally, a first contact electrode and a second contact electrode are formed on the ITO transparent conductive layer and the exposed interface region, respectively.

These and other objectives of the claimed invention will no doubt become obvious to those of ordinary skill in the art after having read the following detailed description of the preferred embodiment that is illustrated in the various figures and drawings.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a cross sectional view of a high brightness light emitting diode having a transparent substrate according to the first embodiment of the present invention.

FIG. 2 is a cross sectional view showing a first semiconductor multilayer before wafer bonding during the manufacturing method according to the present invention.

FIG. 3 is a cross sectional view showing an amorphous interface layer and a second semiconductor multilayer before wafer bonding during the manufacturing method according the present invention.

FIG. 4 is a cross sectional view showing a third semiconductor multilayer after wafer bonding, but before removal of the non-transparent substrate during the manufacturing method according the present invention.

FIG. 5 is a cross sectional view showing a third semiconductor multilayer after removal of the non-transparent substrate and formation of an ITO transparent conductive layer during the manufacturing method according the present invention.

FIG. 6 is a cross sectional view of a high brightness light emitting diode having a transparent substrate according to the second embodiment of the invention.

FIG. 7 is a cross sectional view of a high brightness light emitting diode having a transparent substrate according to the third embodiment of the invention.

FIG. 8 is a cross sectional view of a high brightness light emitting diode having a transparent substrate according to the fourth embodiment of the invention.

DETAILED DESCRIPTION

FIG. 1 is a cross sectional view of a high brightness light emitting diode (LED) 1 having a transparent substrate according to the first embodiment of the present invention. In the LED 1, an indium tin oxide (ITO) amorphous interface layer 11 is formed on a sapphire transparent substrate 10. A top surface of the ITO amorphous interface layer 11 comprises a first surface region and a second surface region. The LED further comprises layers stacked upon each other on the first surface region in the following order, bottom to top: a contact layer of p⁺-type GaAs 12,a cladding layer of a p-type AlGaInP 13, a multiple quantum well (MQW) light-emitting layer 14, a cladding layer of n-type AlGaInP 15, a stop layer of n-type AlGaAs 16, and an ITO transparent conductive layer 18. A first electrode 19 is located on the ITO transparent conductive layer 18, and a second electrode 20 is located on the second surface region.

FIG. 2 and FIG. 3 illustrate a method for manufacturing the light emitting diode 1 according to the first embodiment of the present invention. A first semiconductor multilayer 2 is created by first forming an n-type stop layer 16 of AlGaAs on an n-type GaAs semiconductor substrate 17. Then an n-type cladding layer 15 of AlGaInP is formed on the n-type stop layer 16. An MQW light-emitting layer 14 of AlGaInP is formed on the n-type cladding layer 15. A p-type cladding layer 13 of AlGaInP is formed on the MQW light-emitting layer 14, and a p⁺-type contact layer 12 of GaAs is formed on the p-type cladding layer 13. Next, a second semiconductor multilayer 3 is created. The second semiconductor multilayer 3 comprises an amorphous interface layer 11 of ITO formed on a sapphire substrate 10. As is shown in FIG. 4, a third semiconductor multilayer 4 is produced by inverting the first semiconductor multilayer 2, placing it on the semiconductor multilayer 3, and bonding the first semiconductor multilayer 2 to the second semiconductor multilayer 3 by elevating temperature and applying uniaxial pressure to the semiconductor multilayers. FIG. 4 and FIG. 5 show the next step, which comprises the removal of the n-type GaAs semiconductor substrate 17 from the multilayer 4 and the formation of a first ITO transparent conductive layer 18 on the n-type stop layer 16, producing a fourth semiconductor multilayer 5. Next, an interface exposed region is formed by etching away a portion of the fourth semiconductor multilayer 5 from the first ITO transparent conductive layer 18 to the ITO amorphous interface layer 11. Finally, a first contact electrode 19 and a second contact electrode 20 are formed on the first ITO transparent conductive layer 18 and the interface exposed region, respectively.

FIG. 6 illustrates a light emitting diode 6 having a transparent substrate according to a second preferred embodiment of the present invention. A transparent substrate 611 of p-type GaP is formed on an ohmic contact electrode 610. A first p⁺-type contact layer 612 of GaAs is formed on the transparent substrate 611. An indium tin oxide (ITO) amorphous interface layer 613 is formed on the first p⁺-type contact layer 612. A second p⁺-type contact layer 614 of GaAs is formed on the ITO amorphous interface layer 613. A p-type cladding layer 615 of AlGaInP is formed on the second p⁺-type contact layer 614. A multiple quantum well (MQW) light-emitting layer 616 of AlGaInP is formed on the p-type cladding layer 615. An n-type cladding layer 617 of AlGaInP is formed on the MQW light-emitting layer 616. An n-type stop layer 618 of AlGaAs is formed on the n-type cladding layer 617. An ITO transparent conductive layer 619 is formed on the n-type stop layer 618. An electrode 620 is formed on the ITO transparent conductive layer 619.

FIG. 7 illustrates a light emitting diode 7 having a transparent substrate according to a third preferred embodiment of the present invention. A transparent substrate 711 of n-type GaP is formed on a first electrode 710. An indium tin oxide (ITO) amorphous interface layer 713 is formed on the transparent substrate 711. An n-type contact layer 714 of GaP is formed on the ITO amorphous interface layer 713. An n-type cladding layer 715 of AlGaInP is formed on the n-type contact layer 714. A multiple quantum well (MQW) light-emitting layer 716 of AlGaInP is formed on the n-type cladding layer 715. A p-type cladding layer 717 of AlGaInP is formed on the MQW light-emitting layer 716. A p-type buffer layer 718 of AlGaAs is formed on the p-type cladding layer 717. A p⁺-type contact layer 719 of GaAs is formed on the p-type buffer layer. An ITO transparent conductive layer 720 is formed on the p⁺-type contact layer 719. A second electrode 721 is formed on the ITO transparent conductive layer 720.

FIG. 8 illustrates a light emitting diode 8 having a transparent substrate according to a fourth preferred embodiment of the present invention. An indium tin oxide (ITO) amorphous interface layer 811 is formed on a transparent substrate 810 of glass. A top surface of the ITO amorphous interface layer 811 comprises a first surface region and a second surface region. An n⁺-type reverse tunneling contact layer 814 of InGaN is formed on the first surface region. A p-type cladding layer 815 of GaN is formed on the n⁺-type reverse tunneling contact layer 814. A multiple quantum well (MQW) light-emitting layer 816 of InGaN is formed on the p-type cladding layer 815. An n-type cladding layer 817 of GaN is formed on the MQW light-emitting layer 816. A first Ti—Al contact electrode is formed on the n-type cladding layer 817. A second electrode 820 is formed on the second surface region.

According to the description of these embodiments, LEDs having a transparent substrate can be manufactured by a method of bonding two chips using an amorphous interface layer. LEDs made according to the present invention are easier to manufacture, less expensive to manufacture, and brighter than those made according to the prior art.

While the invention has been disclosed and described with reference to these preferred embodiments, the scope of the invention is not limited to these preferred embodiments. Any variation and modifications of the invention still falls within the spirit and scope of the invention. For example, using a transparent conductive layer of adhesive agent instead of a single-crystal interface layer or using a single quantum well light-emitting layer instead of a multiple quantum well light-emitting layer cannot escape the scope and spirit of the invention. Moreover, the manufacturing method of the present invention is also suitable for manufacturing a light emitting diode having a non-transparent substrate.

Those skilled in the art will readily observe that numerous modifications and alterations of the device may be made while retaining the teachings of the invention. Accordingly, the above disclosure should be construed as limited only by the metes and bounds of the appended claims. 

1. A multilayer structure, comprising: a light-emitting layer having an upper side, a lower side, and a lateral side; an amorphous interface layer, not for growing the light-emitting layer, arranged on the lower side and being distant from the light-emitting layer; and a lower electrode arranged on the lateral side and electrically connected to the amorphous interface layer.
 2. The multilayer structure of claim 1, further comprising: a transparent substrate arranged on the lower side of the light-emitting layer.
 3. The multilayer structure of claim 1, further comprising: an upper electrode arranged on the upper side of the light-emitting layer.
 4. The multilayer structure of claim 1, further comprising: an upper electrode arranged in an oblique direction of the lower electrode.
 5. The multilayer structure of claim 1, wherein the lower electrode is separated from the light-emitting layer.
 6. The multilayer structure of claim 1, wherein the amorphous interface layer has a top surface facing the lower side and not being entirely covered by the light-emitting layer.
 7. A multilayer structure, comprising: a semiconductor multilayer structure adapted to emit light and having an upper surface, a lower surface opposite to the upper surface, and a side surface; an amorphous interface layer arranged on the upper surface and not for growing the semiconductor multilayer structure; and a lower electrode arranged on the amorphous interface layer and separated from the semiconductor multilayer structure.
 8. The multilayer structure of claim 7, further comprising: a substrate arranged on the lower surface.
 9. The multilayer structure of claim 7, further comprising: an upper electrode arranged on the upper surface of the semiconductor multilayer structure.
 10. The multilayer structure of claim 7, further comprising: an upper electrode arranged in an oblique direction of the lower electrode.
 11. The multilayer structure of claim 7, wherein the semiconductor multilayer structure comprises an MQW light-emitting layer distant from the amorphous interface layer.
 12. The multilayer structure of claim 7, wherein the semiconductor multilayer structure is narrower than the amorphous interface layer.
 13. The multilayer structure of claim 7, wherein the amorphous interface layer is elongated past the side surface.
 14. The multilayer structure of claim 7, wherein the lower electrode directly contacts the amorphous interface layer.
 15. A multilayer structure, comprising: a semiconductor multilayer structure adapted to emit light and having a top boundary, a bottom boundary, and a lateral boundary; and an amorphous interface layer, not for growing the semiconductor multilayer structure, arranged under the bottom boundary and beyond the lateral boundary.
 16. The multilayer structure of claim 15, wherein the amorphous interface layer is transparent to the light from the semiconductor multilayer structure.
 17. The multilayer structure of claim 15, wherein the amorphous interface layer is electrically connected to the semiconductor multilayer structure.
 18. The multilayer structure of claim 15, further comprising: an upper electrode arranged above the top boundary; and a lower electrode arranged in an oblique direction of the upper electrode.
 19. The multilayer structure of claim 15, wherein the semiconductor multilayer structure comprises a light-emitting layer distant from the amorphous interface layer.
 20. The multilayer structure of claim 15, wherein the amorphous interface layer is wider than the semiconductor multilayer structure. 